TIOXHUA RUTILE TiO2 XR-290
Description
Titanium Dioxide Coating XR-290—for ink and paint （OR for ink and paint that requires high gloss, and high color performance.）
Typical Properties
High Gloss, High Whiteness and Easy Dispersion
XR-290 is suitable for ink and paint that requires high gloss, and high color performance.
| Processing Method | Sulfate |
| Crystal Form | Rutile |
| Inorganic Surface Treatment | Aluminum Compounds |
| Organic Surface Treatment | Yes |
| Classification (ISO 591-1) | R2 |
| Color (ISO 787-25) | △E≤ 0.5 |
| Relative Scattering Power (ISO 787-24) | 95% - 105% |
| Density (ISO 787-10) | 4.0g/cm3 |
| Dispersion in Polyester System (GB/T 21868.3-2008) | ≤ 27.5μm |
Key Features
High gloss
High whiteness with blue undertone
Easy wetting and dispersing
Product Parameters
| TiO2%（ISO 591-1） | 94% |
| CIE L* (GB/T 1864-2012) | 95.3 |
| Tinting Strength（TCS） | 2080 |
| pH Value（ISO 787-9） | 8 |
| Oil Absorption（ISO 787-5） | 16g/100g |
| Residue on 45μm sieve（ISO 787-18） | 0.01% |
| Resistivity（ISO 787-14） | > 100 Ω·m |
| Volatiles at 105℃（ISO 787-2）at packaging | 0.3% |
More Product Information
Health and Safety Precautions
Relevant local health and safety guidelines should be followed. Gloves, safety goggles and respirator with submicron particle filtration should be worn. MSDS is available upon request.
Packaging
XR-290 is available in 25kg bags, 500kg and 1000kg containers.
Product Storage
Product should be stored indoors in clean and dry conditions. The shelf life of CHTi’s TiO2 is 2 years if stored properly. First-in, first-out regime is highly recommended to ensure the performance of the product.
Disclaimer
Above information is offered free solely for purpose of providing possible suggestions. Given variations in actual end-use conditions, CHTi makes no warranties and assumes no liability in connection with any use of this information.
Gallery
Get In Touch
Request More Product Details
Interested in this product? Send us your inquiry and our team will get back to you with pricing, specifications, samples, and more details as soon as possible.